Electrodeposition of Co-Ni-Fe on Stainless Steel Bolts

  • Authors

    • M. S. Md.Nor
    • Z. Salleh
    • N. R. N. M. Masdek
    • Y. M Taib
    • M. Z. Abu
    2018-11-30
    https://doi.org/10.14419/ijet.v7i4.26.22171
  • Bolt, Co-Ni-Fe, Electrodeposition, Stainless steel 304, Surface properties.

  • In a fastening system, bolt is the first component to be susceptible to corrosive attack. The focus of the study is to investigate the feasibility of coating stainless steel 304 bolts and the coating properties obtained. In this study, the bolts were coated with cobalt-nickel-iron (Co-Ni-Fe) alloy through electrodeposition using platinized titanium as the anodes. The temperature used was 50°C and the pH of the sulphate solution were 2. The current density was 96.68 mA/cm2 and deposition time was 30 minutes. The optimum electrodeposition parameters were studied through trial and error. The characteristics of coating such as elemental percentage and microhardness were compared with the substrate. The optimum parameters obtained were current density of 145.01 mA/cm2, temperature of 60°C and 30 minutes of deposition time. The suitable substrate orientation was horizontally hanged and rotated 60° around screw axis for every 5 minutes. The mean thickness of coating was 117.4 µm. The coating exhibited 25% hardness improvement over the substrate. The 2 litres solution could be used for 7.5 hours (15 plating cycles) to produce 15 samples. As a conclusion the surface hardness was not compromised despite that Co-Ni-Fe ions had depleted in the solution.

     

  • References

    1. [1] F. A. Lowenheim and S. Senderoff, Modern Electroplating, vol. 111, no. 11. 1964.

      [2] R. W. Revie and H. H. Uhlig., Corrosion and Corrosion Control: An Introduction to Corrosion Science and Engineering, 4th Edition. 2008.

      [3] M. H. Koay, M. A. A. Tukiran, S. N. A. Mohd Halidi, M. Che Murad, Z. Salleh, and H. Yusoff, “Corrosion investigation of Co–Ni–Fe-coated mild steel electrodeposited at different current densities and deposition times,†Ind. Lubr. Tribol., vol. 69, no. 3, pp. 393–398, 2017.

      [4] K. M. Hyie, M. Z. Zabri, N. R. Nik Roseley, and N. R. Nik Mohd Masdek, “Effect of deposition time on wear and corrosion performance of Co–Ni–Fe alloy coated mild steel,†J. Mater. Res., vol. 31, no. 13, pp. 1848–1856, 2016.

      [5] Bolt Depot Inc., “Tap bolts.†[Online]. Available: https://www.boltdepot.com/Tap_bolts.aspx. [Accessed: 21-Apr-2018].

      [6] C. Evans, Metrology and properties of engineering surfaces, vol. 1, no. 3. 1979.

      [7] Plating Resources Inc., “Poor Throwing Power & Coverage.†[Online]. Available: http://www.plating.com/platingtechnical/poorthrowingpower.htm. [Accessed: 09-Jun-2018].

      [8] T. Winn, “What Is ‘Burning’ from a Plating Bath?,†2016. [Online]. Available: https://www.asterionstc.com/2016/04/burning-plating-bath/. [Accessed: 27-Jun-2018].

      [9] “Brass Electroplating.†[Online]. Available: http://shodhganga.inflibnet.ac.in/bitstream/10603/181590/6/06_chapter 3.pdf. [Accessed: 20-Apr-2018].

      [10] M. Carano, “Trouble in Your Tank: Acid Copper Plating,†2017. [Online]. Available: http://pcb.iconnect007.com/index.php/article/102516/trouble-in-your-tank-acid-copper-plating/102519/?skin=pcb. [Accessed: 04-May-2018].

      [11] N. Once, “5 Troubleshooting,†pp. 40–41.

      [12] T. George, K. Son, B. Eyre, O. Orient, M. Jpl, P. K. Nobe, P. Sumodjo, D. Park, and B. Yoo, “Development of electroplated magnetic materials for MEMS,†J. Magn. Magn. Mater., vol. 265, no. 2, p. 192, 2003.

      [13] Lumen Learning, “Predicting the Products of Electrolysis.†[Online]. Available: https://courses.lumenlearning.com/boundless-chemistry/chapter/electrolysis/. [Accessed: 13-May-2018].

      [14] AZoM, “Using EDS and WDS for the Examination of the Fluorine K Line and Iron L Line Overlap.†[Online]. Available: https://www.azom.com/article.aspx?ArticleID=11971. [Accessed: 20-May-2018].

      [15] P. Harvey, Engineering Properties of Steel. 1982.

      [16] AZoM, “Stainless Steel - Heat Treatment,†2002. [Online]. Available: https://www.azom.com/article.aspx?ArticleID=1141#hardening. [Accessed: 07-Jun-2018].

      [17] K. M. Hyie, N. A. Resali, and W. N. R. Abdullah, “Study of Alloys Addition to the Electrodeposited Nanocrystalline Cobalt,†Adv. Mater. Res., vol. 486, pp. 108–113, 2012.

  • Downloads

  • How to Cite

    S. Md.Nor, M., Salleh, Z., R. N. M. Masdek, N., M Taib, Y., & Z. Abu, M. (2018). Electrodeposition of Co-Ni-Fe on Stainless Steel Bolts. International Journal of Engineering & Technology, 7(4.26), 221-225. https://doi.org/10.14419/ijet.v7i4.26.22171