Effect of La3+ Substitution at Bi-Site on Transport Properties of Bi0.3-xLaxPr0.3Ca0.4Mn0.1Cr0.9MnO3

  • Authors

    • Norazila Ibrahim
    • Nor Asmira Amaran
    • Zakiah Mohamed
    • Ahmad Kamal Yahya
    2019-12-24
    https://doi.org/10.14419/ijet.v7i4.14.27773
  • A-Site substitution, Electrical conductivity, Magnetoresisatnce
  • Magnetic and electronic transport properties of Bi0.3-xLaxPr0.3Ca0.4Mn0.1Cr0.9O3 (0≤x≤0.2) manganites have been investigated by measurements of AC-susceptibility, resistivity and magnetoresistance. The samples were prepared using conventional solid-state synthesis method. Magnetic susceptibility versus temperature measurements showed all samples exhibit ferromagnetic to paramagnetic transition with Curie temperature, Tc enhanced from 111 K (x=0) to 174 K (x=0.2). Electrical resistivity measurements of the samples in zero field showed increase of metal-insulator (MI) transition temperature from 58 K(x=0) to 88 K(x=0.2). The increase in both Tc and TMI indicates enhancement of double exchange (DE) interaction involving Mn3+ and Mn4+ ions as a result of weakening of the hybridization effect between Bi3+ 6s2 lone pair with O orbital due to La3+ substitution.  La substitution in the Bi-based compound is suggested reduce MnO6 octahedral distortion hence increasing delocalization of charge carriers. The observed variation in MR behavior due to La substitution indicates the substitution influence the MR mechanism of extrinsic and intrinsic behavior in Bi0.3-xLaxPr0.3Ca0.4Mn0.1Cr0.9O3 .

     

  • References

    1. [1] N. Ibrahim and A. K. Yahya, “Inducement of Itinerant Electron Transport in Charge-Ordered Pr0.6Ca0.4MnO3 by Ba Dopingâ€, J. Supercond. Nov. Magn., vol 911, 2016.

      [2] C.S. Xiong, F.F.Wei, et al, “Electrical properties and magnteelectric effect measurement in La0.7Ca0.2Sr0.1MnO3/xCoFe2O3 compositesâ€, Journal of Alloy and Compounds , vol 474, pp. 316-320, 2009.

      [3] N.Ibrahim, A.K.Yahya, “Enhancement of extrinsic magnetoresistance behaviour in BiFeO3 doped La0.8Ag0.2MnO3 ceramicâ€, Ceramics International , vol39, pp.S181-S184, 2013.

      [4] R.Rozilah, N.Ibrahim, Z.Mohamed,A.k.Yahya, NawazishA.khan, M.Nasir Khan, “Inducement of ferromagnetic-metallic phase in intermediate charge -ordered Pr0.25Na0.25MnO3 manganite by K+ substitutionâ€, Phys B. Condens. Matter , vol 521 pp. 281-294, 2017.

      [5] Kamlesh Yadav,H K Singh and G D Varma, “Effect of La-doping on magnetic properties of Bi0.6-xLaxCa0.4MnO3 (0.0≤ x≤0.6) perovskite manganitesâ€, Phys.Scripta, vol 85 , pp. 6 pages 045704, 2012.

      [6] Ben Jazia Kharrat, S. Moussa, N. Moutiaa, K. Khirouni, W. Boujelben, “Structural, electrical and dielectric properties of Bi-doped Pr0.8-xBixSr0.2MnO3 manganite oxides prepared by sol-gel processâ€, Journal of Alloys and Compounds, vol 724, pp. 389-399, 2017..

      [7] N. Asmira, N. Ibrahim, Z. Mohamed and A.K. Yahya, “Effect of Cr3+ substitution at Mn-site on electrical and magnetic properties of charge ordered Bi0.3Pr0.3Ca0.4MnO3 manganitesâ€, Physica B, vol 544, pp.34-46, 2018.

      [8] C. Zener, Interaction between the d-shells in the transition metals II. Ferromagnetic compounds of manganese with perovskite structure, Phys. Rev, vol 82, pp.403, 1951.

      [9] A.J. Millis, P.B. Littlewood, B.I. Shraiman, “Double exchange alone does not explain the resistivity of La1-xSrxMnO3â€, J. Phys. Rev. Lett., vol 74, pp. 5144-5147, 1955.

      [10] Tokura, Y. Tomioka, H. Kuwahara, A. Asamitsu, Y. Moritomo and M. Kasai, “Origins of colossal magnetoresistance in perovskiteâ€type manganese oxidesâ€, Journal of Applied Physics, vol 79, pp.5288-5291, 1996.

      [11] Jin, T.H. Tiefel, M. McCormack, R.A. Fastnacht, R. Ramesh and L.H. Chen, “Thousandfold change in resistivity in magnetoresistive La-Ca-Mn-O filmsâ€, Science, vol 264, pp. 413-415, 1994.

  • Downloads

  • How to Cite

    Ibrahim, N., Asmira Amaran, N., Mohamed, Z., & Kamal Yahya, A. (2019). Effect of La3+ Substitution at Bi-Site on Transport Properties of Bi0.3-xLaxPr0.3Ca0.4Mn0.1Cr0.9MnO3. International Journal of Engineering & Technology, 7(4.14), 478-781. https://doi.org/10.14419/ijet.v7i4.14.27773