Low Temperature Fabrication of Flower-Like Rutile Phased Tio2 Film towards Methyl Orange Degradation

  • Authors

    • N. K. A. Hamed
    • M. K Ahmad
    • M. H. Mazlan
    • N. H.H. Hairom
    • N. Nafarizal
    • C. F. Soon
    • R. Sanudin
    • H. S. Aziz
    • M. H. Mamat
    • A. B. Suriani
    • M. Shimomura
    • K. Murakami
    2019-01-18
    https://doi.org/10.14419/ijet.v8i1.7.25955
  • Rutile, flower-like, TiO2, photocatalytic
  • Pure rutile titanium dioxide (TiO2) thin film was fabricated at a low temperature of 150oC by using a simple, one step hydrothermal method. TiO2 thin film was developed on Fluorine doped tin oxide (FTO) by using titanium butoxide (TBOT) as a precursor, hydrochloric acid (HCl) and deionized (DI) water. The assembly of flower-like rutile phased TiO2 could be controlled by simply changing the amount of precursors. The prepared samples were characterized by using Field Emission Scanning Electron Microscopy, X-ray Diffraction and Energy-dispersive spectroscopy. Most importantly, this pure rutile TiO2 thin film showed a great significance compared to commercial TiO2 Degussa P25 on degradation of methyl orange under UV light. The degradation of rutile TiO2 thin film was up to 65.6 % while P25 thin film was only 8.07 %. From the experiments, it was found that the rutile phased TiO2 has the higher photocatalytic activity in lower MO concentration and favorable in acidic environment. The enhanced activity might be accredited to the efficient separation of electron-hole pairs and high surface area produced by flower-like rutile phased TiO2.

     

  • References

    1. [1] J. Vázquez-samperio, N. M. Sánchez-padilla, and P. Acevedo-peña, “Ni Prussian Blue Analogue / Mesoporous Carbon Composite as Electrode Material for Aqueous K-Ion Energy Storage : Effect of Carbon-Framework Interaction on Its Electrochemical Behavior,†pp. 11441–11450, 2018.

      [2] E. Photovoltaic and S. Energy, “19th European Photovoltaic Solar Energy Conference, 7-11 June 2004, Paris, France,†no. June, pp. 305–308, 2004.

      [3] H. Y. Hafeez and I. Ibrahim, “Effect Of Annealing Temperature On The Electrical Properties Of Titanium Dioxide ( Tio 2 ) -Roselle Dye Sensitized Solar Cell . International Journal Of Advanced Research ( Ijar ) International Journal Of Advanced Research ( Ijar ),†no. September, 2016.

      [4] K. P. Biju and M. K. Jain, “Effect of crystallization on humidity sensing properties of sol – gel derived nanocrystalline TiO 2 thin films,†vol. 516, pp. 2175–2180, 2008.

      [5] J. Domaradzki, “Structural, optical and electrical properties of transparent V and Pd-doped TiO2 thin films prepared by sputtering,†Thin Solid Films, vol. 497, no. 1–2, pp. 243–248, Feb. 2006.

      [6] N. Orleans, “Structure and properties of TiO 2 surfaces :,†vol. 687, no. 2003, pp. 681–687, 2004.

      [7] N. Sasirekha, B. Rajesh, and Y. Chen, “Synthesis of TiO 2 sol in a neutral solution using TiCl 4 as a precursor and H 2 O 2 as an oxidizing agent,†vol. 518, pp. 43–48, 2009.

      [8] B. Liu and E. S. Aydil, “Growth of oriented single-crystalline rutile TiO2 nanorods on transparent conducting substrates for dye-sensitized solar cells,†J. Am. Chem. Soc., vol. 131, no. 9, pp. 3985–3990, 2009.

      [9] Y. Tao, Z. Han, Z. Cheng, Q. Liu, F. Wei, and K. E. Ting, “Synthesis of Nanostructured TiO 2 Photocatalyst with Ultrasonication at Low Temperature,†no. January, pp. 29–36, 2015.

      [10] M. Pelaez, N. T. Nolan, S. C. Pillai, M. K. Seery, P. Falaras, A. G. Kontos, P. S. M. Dunlop, J. W. J. Hamilton, J. A. Byrne, K. O. Shea, M. H. Entezari, and D. D. Dionysiou, “Applied Catalysis B : Environmental A review on the visible light active titanium dioxide photocatalysts for environmental applications à¬,†"Applied Catal. B, Environ., vol. 125, pp. 331–349, 2012.

      [11] N. N. & M. K. A. Noor Kamalia Abd Hamed*, Noor Sakinah Khalid, Fatin Izyani Mohd Fazli, Muhammad Luqman Mohd Napi, “Influence of Hydrochloric Acid Volume on the Growth of Titanium Dioxide ( TiO 2 ) Nanostructures by Hydrothermal Method,†Sains Malaysiana, vol. 45, no. 11, pp. 1669–1673, 2016.

      [12] Y. Wang, L. Zhang, K. Deng, X. Chen, and Z. Zou, “Low Temperature Synthesis and Photocatalytic Activity of Rutile TiO2 Nanorod Superstructures,†J. Phys. Chem. C, vol. 111, no. October, pp. 2709–2714, 2007.

      [13] K. H. Ng, M. R. Deraman, C. H. Ang, and S. K. Chong, “Phototreatment of Palm Oil Mill Effluent ( POME ) over Cu / TiO 2 Photocatalyst,†BCREC, vol. 9, no. 2, pp. 121–127, 2014.

      [14] I. Sopyan, M. Watanabe, S. Murasawa, K. Hashimoto, and A. Fujishima, “An efficient TiO2 thin-film photocatalyst : photocatalytic properties in gas-phase acetaldehyde degradation,†vol. 6030, no. 96, 1996.

      [15] F. R. F. Fan and A. J. Bard, “Semiconductor electrodes. 24. Behavior of photoelectrochemical cells based on p-type gallium arsenide in aqueous solutions,†vol. 102, no. May, pp. 3677–3683, 2002.

      [16] M. A. Lazar, S. Varghese, and S. S. Nair, “Photocatalytic water treatment by titanium dioxide: recent updates,†Catalyst, vol. 2, pp. 572–601, 2012.

      [17] S. Lee and S. Park, “Journal of Industrial and Engineering Chemistry TiO 2 photocatalyst for water treatment applications,†vol. 19, pp. 1761–1769, 2013.

      [18] Y. B. Xie and X. Z. Li, “Preparation and characterization of TiO 2 / Ti film electrodes by anodization at low voltage for photoelectrocatalytic application,†pp. 663–668, 2006.

      [19] K. Song and K. A. Gray, “Growth of rutile TiO 2 nanorods on anatase TiO 2 thin fi lms on Si-based substrates,†2011.

      [20] T. Wen, J. Gao, and J. Shen, “Preparation and characterization of TiO 2 thin films by the sol-gel process,†vol. 6, pp. 5923–5926, 2001.

      [21] T. R. Pauly, Y. Liu, T. J. Pinnavaia, S. J. L. Billinge, and T. P. Rieker, “Textural mesoporosity and the catalytic activity of mesoporous molecular sieves with wormhole framework structures,†J. Am. Chem. Soc., vol. 121, no. 7, pp. 8835–8842, 1999.

      [22] Ã. A. R.-S. P. Acevedo-Peña and E. M. Córdoba, “Enhanced photocatalytic activity of TiO2 film by modification with polyethylene glycol,†Quim. Nov., vol. 35, no. 10, pp. 1931–1935, 2012.

      [23] B. Neppolian, H. C. Choi, S. Sakthivel, B. Arabindoo, and V. Murugesan, “Solar/UV-induced photocatalytic degradation of three commercial textile dyes,†J. Hazard. Mater., vol. 89, no. 2–3, pp. 303–317, 2002.

      [24] S. Al-qaradawi and S. R. Salman, “Photocatalytic degradation of methyl orange as a model compound,†Photochem. Photobiol., vol. 148, pp. 161–168, 2002.

      [25] R. J. Davis, J. L. Gainer, and G. O. Neal, “Photocatalytic decolorization of wastewater dyes,†Water Environ. Res., vol. 66, no. 1, pp. 50–53, 1989.

      [26] Z. Haddadian, M. A. Shavandi, Z. Zainal, M. Halim, and S. Ismail, “Removal methyl orange from aqueous solutions using dragon fruit (hylocereusundatus) foliage,†Chem. Sci. Trans., vol. 2, no. 3, pp. 900–910, 2013.

      [27] M. Kosmulski, “The significance of the difference in the point of zero charge between rutile and anatase,†Adv. Colloid Interface Sci., vol. 99, pp. 255–264, 2002.

      [28] A. P.Davis and C. p. Huang, “The removal of substituted phenols by a photocatalytic oxidation process with cadmium sulfide,†Water Res., vol. 24, no. 5, pp. 543–550, 1990.

      [29] M. Ye, H.-Y. Liu, C. Lin, and Z. Lin, “Hierarchical rutile TiO2 flower cluster-based high efficiency dye-sensitized solar cells via direct hydrothermal growth on conducting substrates.,†Small, vol. 9, no. 2, pp. 312–21, Jan. 2013.

  • Downloads

  • How to Cite

    K. A. Hamed, N., K Ahmad, M., H. Mazlan, M., H.H. Hairom, N., Nafarizal, N., F. Soon, C., Sanudin, R., S. Aziz, H., H. Mamat, M., B. Suriani, A., Shimomura, M., & Murakami, K. (2019). Low Temperature Fabrication of Flower-Like Rutile Phased Tio2 Film towards Methyl Orange Degradation. International Journal of Engineering & Technology, 8(1.7), 49-55. https://doi.org/10.14419/ijet.v8i1.7.25955